Just curious if its a bad idea to run raw aluminum parts, or if its okay. Or does it more depends on what the item is?
-
-
It’s best to anodize. Raw aluminum is soft it will pit and mar easily. The process of anodizing actuality hardens the material.
I would avoid playing with raw aluminum parts.-
Thanks. I'm very familiar with anodizing, did a lot at my previous job. Just wasn't sure if our application would tolerate raw parts or not. Thanks! -
A grip maybe or a feed because it’s can easily be polished out would be fine for a lil while. But anything internal not easily polished I wouldn’t take the chance. It’s best to wait for Ano. Oils and paint will slowly damage raw parts.
-
-
In this case, it's a grip frame. I've already contacted ARC and they said no problem.
Just have to decide on the color now.Comment